Zirconia mullite, simply, is a mullite containing zirconia.In order to further improve the corrosion resistance and thermal shock resistance of zirconium mullite and reduce the coefficient of expansion, ZrO2 was introduced into al2O3-SiO2 system to improve the structure of mullite.

Sunrise fused cast zirconia mullite use high-quality bauxite and zircon sand and other raw materials, melting in an arc furnace at high temperature, casting completed.Mainly used for wear - resistant, high - temperature material parts.

Product Characteristics:
Compact structure.
wear-resisting.
Impact resistance.
Strong thermal shock resistance.
Good corrosion resistance and slag resistance.

Application:
Sliding track brick for metallurgical pusher type reheating furnace.
Steel outlet platform of stepping furnace (steel outlet tank).
The sizing nozzle and long nozzle of continuous casting bag.
Lining of refuse incinerator.

The key part of glass melting furnace.

Item			Behaviors TY-GM5
			Special	Typical
Chemical Composition %	Al2O3		71-74	73
	ZrO2		4.5-6	5.5
	SiO2		17-20	19
	Fe2O3		≤0.5	0.5
	Na2O		≤1.0	1.0
	CaO		≤0.5	0.5
Apparent Prosity (%)			5-8	<8
True density g/cm3			≥3.0	3.54
Cold Crushing Strength Mpa			≥250	350
Hot Crushing Strength 1300℃ Mpa				45
Exudation temperature of Glass phase℃
Line Expansion 1150℃ %				0.9
Thermal conductivity 1250 ℃: W/MK				4.6
Bulk Density (g/cm3)		PT(RN)		≥3.0
		WS(VF)		≥3.2
Crystallographic analysis %	Corundum		39
	Mullite		41
	Glass Phase		15
	Baddeleyite		5

Application: for skid rails refractories of steel reheating furnace,

It is mainly used in areas that require high abrasion and temperature resistance, such as gliding rail bricks in steel pusher metallurgical furnaces, the tapping platform (tapping spout) style walking beam furnaces, and also as the interior for destructors.