Dense Zircon Block Back

Dense Zircon Block
  • Apparent Porosity: ≤18%
  • Bulk Density: ≥3.65 g/cm3)
  • Cold Crushing Strength: ≥100 Mpa
  • 0.2Mpa Refractoriness Under Load T0.6: ≥1650 ℃
  • Pyrometric Cone Equivalent S.C. SK : 40
  • Reversible Thermal Expansion 1000℃: 0.5%

Features

Dense zircon brick ZS-65 is a kind of fire brick. The zircon content of it is equal to or greater than 65 percent. It possesses many advantages as high bulk density, low apparent porosity, high cold crushing strength and high refractoriness under load. It is widely used in glass industry and metallurgical industry.

Applications
Dense Zircon brick is widely used in the upper area of flame space and frequent thermal shock region of alkali-free or low-alkali glass, sodium-calcium glass, boron-silicate glass, lead glass and other technical glass melting furnace. It can be also used in transition region between up roof silica brick and fusion zirconia-corundum brick or fusion zirconia-mullite brick, transition region between silica brick and magnesia brick, crown, burner, thermal couple, peep hole, secondary layer of melting bottom and back lining. In addition, it is also applied as the ladle lining for metallurgical industry.
The main applications:
It is mainly applied in the neutral course in tank superstructure and sealing course in tank bottom.

Advantages
High density;
Superior quality;
Accurate size tolerance;
Luster apperance;
High bulk density;
Low apparent porosity;
High cold crushing strength;
High refractoriness under load.

Parameter

 
 
Item ZS-65
ZrO2 (%) ≥65
SiO2 (%) ≤33
Fe2O3(%) ≤0.5
Apparent Porosity (%) ≤18
Bulk Density (g/cm3) ≥3.65
Cold Crushing Strength (Mpa) ≥100
0.2Mpa Refractoriness Under Load T0.6 ℃ ≥1650
Pyrometric Cone Equivalent S.C. SK 40
Reversible Thermal Expansion 1000℃ % 0.5