Silica Brick Back

Silica Brick
Silica Brick
Silica Brick
Silica Brick
Silica Brick
Silica Brick
  • Refractoriness ℃ : 1710
  • Apparent Porosity% : ≤22
  • Bulk Density g/cm3: ≥1.8
  • True Density,g/cm3: ≤2.38
  • Cold Crushing Strength Mpa: ≥24.5
  • 0.2Mpa Refractoriness Under Load T0.6 ℃: ≥1630

Features

Description
Adopts high quality silica and advanced technology, our silica bricks enjoy the advantages of high purity, long service life, good thermal conductivity, high refractoriness under load, and good creep resistance. In addition, it has accurate size tolerance, pure color and luster appearance. Because of the bad thermal shock resistance of silica brick, it is mainly used in the continuous operating furnace. Supporting the use of other high quality refractories, our silica brick can extent the service life of float glass furnace to 8 years and double the service life of bottle glass furnace. It is widely used in coke oven, hot blast furnace, glass furnace and carbon furnace.

Applications
The silica brick can be widely used in coke oven, hot blast furnace, glass furnce and carbon furnace. In glass industry, it is mainly employed to build the doghouse crown, suspended wall of channel, top crown and inlet sealing. In metallurgy industry, it is adopted as the nozzle brick.

The main applications
► Doghouse crown, suspended wall of channel, top crown and inlet sealing of glass furnace
► High temperature part of coke oven.

Specifications
► High purity
► Long service life
► Accurate size tolerance
► Pure color
► Luster appearance

Advantages
► Good thermal conductivity
► High refractoriness under load
► Good creep resistance
► High refractoriness

Parameter

Item BG-94 BG-95 BG-96A BG-96B
Chemical composition SiO2 ≥94 ≥95 ≥96 ≥96
 

 

Fe2O3 ≤1.5 ≤1.5 ≤0.8 ≤0.7
 

 

Al2O3+TiO2+R2O  

 

≤1.0 ≤0.5 ≤0.7
Refractoriness ℃ 1710 1710 1710 1710
Apparent Porosity% ≤22 ≤21 ≤21 ≤21
Bulk Density g/cm3 ≥1.8 ≥1.8 ≥1.8 ≥1.8
True Density,g/cm3 ≤2.38 ≤2.38 ≤2.34 ≤2.34
Cold Crushing Strength Mpa ≥24.5 ≥29.4 ≥35 ≥35
0.2Mpa Refractoriness Under Load T0.6 ℃ ≥1630 ≥1650 ≥1680 ≥1680
Permanent Linear Change On Reheating (%)1500℃X2h 0~+0.3 0~+0.3 0~+0.3 0~+0.3
20-1000℃ Thermal Expansich10-6/℃ 1.25 1.25 1.25 1.25
Thermal Conductivity (W/MK) 1000℃ 1.74 1.74 1.44 1.44