Fused Cast High Zirconia Block Back

Fused cast high zirconia block
Fused cast high zirconia block
Fused cast high zirconia block
Fused cast high zirconia block
Fused cast high zirconia block
Fused cast high zirconia block
  • SiO2 Chemical Composition %: 9.00
  • ZrO2 Chemical Composition % : 89.00
  • Baddeleyite Mineral Composition %: 89
  • Glass Phase Mineral Composition %: 11
  • Bulk Density (g/cm³) : 5.10
  • Liner Thermal Expansion (%) : 0.65

Features

The series of TY-Z are fused cast high zirconia refractories.

They are made of artificial synthesis of high purity raw materials through special casting process. The crystalline texture is consisting of baddeleyite.

So the characteristics of these products are excellent corrosion resistance and very low blister and stoning potential. These advantages can prevent liquid glass from pollution effectively. TY-Z can be used in a wide range of glass furnace, especially high quality and special glass furnaces such as TV glass, Borosilicate glass, Alumina silicate glass, Halogen lighting glass, Opal glass and Fiber glass. TY-Z are mainly consisting of TY-Z88-WS and TY-Z95-WS, and used in sidewall, throat cover, throat support, electrode block, dam block parts.

Parameter

  Item TY-Z88-WS TY-Z95-WS
Chemical Composition % ZrO2 89.00 93.60
  SiO2 9.00 5.30
  Al2O3 1.00 1.00
  Na2O 0.05 0.51
  Others 1.60 1.0
Mineral Composition % Baddeleyite Typical 89 94
  Glass Phase   11 6
Physical Properties Cold Crushing Strength (MPa) 400 400
  Bulk Density (g/cm³) Typical 5.10 5.30
  Liner Thermal Expansion (%) 1000℃ 0.65 0.70
    1500℃ 0.10 0.30