Fused Cast AZS TY-AZS36
Back
- Bulk density g/cm3: ≥3.85
- Apparent Porosity %: ≤1.0
- Cold Crushing Strength Mpa: ≥300
- Exudation Temperature of Glass Phase: ≥1400
- Bubble Separation Ratio（1300℃×10h）: ≤1.4
- Anti-corrosion rate of glass liquid 1500℃×36h （mm/24h）%: ≤1.3
Features
Advantages:
♦ Compact microstructure
♦ Good erosion resistibility to molten glass
♦ Good thermal shock resistibility
♦ Barely rendering blister
TY- AZS36 Shapes and sizes:
This product is only available for straight brick.
Application:
mainly used for side walls of flame furnaces with embedded melter bottoms, for total security with average pulls and campaign lengths, and superstructures, front wall, back wall, top crown in glass melting furnace.
Parameter
| Item | Behaviors | |
| TY-AZS36 | ||
| Chemical Composition | Al2O3 | ≥49.00 |
| ZrO2 | ≥35.50 | |
| SiO2 | ≤13.50 | |
| Na2O+K2O | ≤1.35 | |
| Bulk density g/cm3 | ≥3.85 | |
| Apparent Porosity % | ≤1.0 | |
| Cold Crushing Strength Mpa | ≥300 | |
| Exudation Temperature of Glass Phase | ≥1400 | |
| Bubble Separation Ratio（1300℃×10h） | ≤1.4 | |
| Anti-corrosion rate of glass liquid 1500℃×36h （mm/24h）% | ≤1.3 | |
| Apparent density （g/cm3） | PT(RN RC N) | ≥3.50 |
| ZWS(RR EVF EC ENC) | ≥3.70 | |
| WS( RT VF EPIC FVP DCL) | ≥3.80 | |